INTRODUCTION OF MESOPOROSITY IN LOW Si/Al ZEOLITES

ABSTRACT

Compositions and methods for preparing mesoporous materials from low Si/Al ratio zeolites. Such compositions can be prepared by acid wash and/or isomorphic substitution pretreatment of low Si/Al ratio zeolites prior to introduction of mesoporosity.

RELATED APPLICATIONS

This application claims the benefit of U.S. patent application Ser. No. 12/689,127 entitled Introduction of Mesoporosity in Low Si/Al Zeolites, filed Jan. 18, 2010, which claims benefit of U.S. Provisional Patent Application Ser. No. 61/145,724 entitled Introduction of Mesoporosity in Low Si/Al USY Zeolite and the Effect of Drying Conditions on Mesoporosity Introduction filed Jan. 19, 2009, the entire disclosures of which are incorporated herein by reference.

BACKGROUND

1. Field

One or more embodiments of the invention relate to compositions and methods for preparing mesoporous materials from low Si/Al zeolites.

2. Description of Related Art

Previously, methods have been described to introduce mesoporosity into zeolites, for example, in U.S. Patent Application Publication No. 2007/0244347. These zeolites have a high silicon-to-aluminum ratio (“Si/Al”) and low extra-framework content, namely, ultrastable zeolite Y (“USY”) CBV 720 provided by Zeolyst International.

As previously described, this zeolite can be treated in the presence of a pore forming agent (for example, a surfactant) at a controlled pH under a set of certain time and temperature conditions to introduce mesoporosity into the zeolite. Thereafter, the mesostructured material can be treated to remove the pore forming agent (for example by calcination or chemical extraction).

Zeolites used in fluid catalytic cracking (“FCC”) can have larger unit cell sizes than that of CBV 720 (see Table 1). For example, USY zeolite CBV 500, also from Zeolyst, may be a more suitable raw material for FCC applications. Additionally, NH₄Y CBV 300, also from Zeolyst, may be suitable for such uses. As shown in Table 1, USY CBV 500 and NH₄Y CBV 300 both have larger unit cell sizes, namely 24.53 Å and 24.70 Å, respectively, than USY CBV 720, namely 24.28 Å.

The CBV 500 zeolite contains a significant amount of extra-framework alumina (“EFAL”), due to the leach of some framework alumina (“FA”), as revealed by a decrease in the unit cell size from parent NaY (see Table 1). USY CBV 720, a more stabilized zeolite Y, has a much smaller unit cell size, and a reduced EFAL content, due to an acid wash following a severe stabilization treatment (e.g., steaming). CBV 300 zeolite has a low EFAL content, presumably because it is not subjected to heat treatment.

An EFAL content is the percent total of aluminum that has low extra-framework alumina. From 0-10% can be considered to be a low EFAL content whereas an EFAL content from 25-100% can be considered to be a high EFAL content.

TABLE 1 Physicochemical Characteristics of Zeolites Provided by Zeolyst Int'l NaY NH₄Y USY USY CBV 100 CBV 300 CBV 500 CBV 720 Unit Cell (Å) 24.65 24.70 24.53 24.28 EFAL Low Low High Low content Si/Al 2.6 2.6 5.2 30 ratio (total) Cation Sodium Ammonium Ammonium Proton

When the treatment described in previous patent applications to introduce mesoporosity in CBV 720 was used to introduce mesoporosity in CBV 500, no appreciable amount of mesoporosity was observed. In addition, no major change in the physicochemical characteristic of CBV 500 was observed. Similar absences of change were observed for CBV 300 and CBV 100 when subjected to the same treatments.

SUMMARY

One embodiment of the present invention concerns a method of forming a material comprising at least one mesostructured zeolite. The method of this embodiment comprises the steps of: (a) acid washing an initial zeolite with an acid thereby forming an acid-washed zeolite, where the initial zeolite has a total silicon-to-aluminum ratio (Si/Al) of less than 30; and (b) forming at least one mesopore within the acid-washed zeolite thereby forming the mesostructured zeolite.

Another embodiment of the present invention concerns a method of forming a material comprising at least one mesostructured zeolite. The method of this embodiment comprises the steps of: (a) acid washing an initial zeolite with an acid thereby forming an acid-washed zeolite, where the initial zeolite has an average unit cell size of at least 24.40 Å; and (b) forming at least one mesopore within the acid-washed zeolite thereby forming the mesostructured zeolite.

Still another embodiment of the present invention concerns a method of forming a material comprising at least one mesostructured zeolite. The method of this embodiment comprises the steps of: (a) providing an initial zeolite; (b) isomorphically substituting at least a portion of the framework aluminum in the initial zeolite with framework silicon to thereby form an isomorphically-substituted zeolite; and (c) forming at least one mesopore within the isomorphically-substituted zeolite thereby forming the mesostructured zeolite.

Yet another embodiment of the present invention concerns a method of forming a material comprising at least one mesostructured zeolite. The method of this embodiment comprises the steps of: (a) acid-washing an initial zeolite having a low silicon-to-aluminum ratio with an acid thereby forming an acid-washed zeolite; and (b) forming at least one mesopore within the acid-washed zeolite thereby forming the mesostructured zeolite.

BRIEF DESCRIPTION OF THE DRAWING FIGURES

Embodiments of the present invention are described herein with reference to the following drawing figures, wherein:

FIG. 1 is a graph depicting nitrogen physisorption isotherms at 77K of zeolite before (square data points) and after (diamond data points) having been treated with ammonium hexafluorosilicate;

FIG. 2 a is a graph depicting nitrogen physisorption isotherms at 77K of CBV 720 before (diamond data points) and after (square data points) having been treated as described in Example 1;

FIG. 2 b is a pore size distribution plot obtained using non-linear density functional theory of the material produced in Example 1;

FIG. 3 a is a graph depicting an argon physisorption isotherm at 87K of CBV 500 after having been treated as described in Example 2;

FIG. 3 b is a pore size distribution plot obtained using non-linear density functional theory of the material produced in Example 2;

FIG. 4 a is a graph depicting argon physisorption isotherms of CBV 500 before (square data points) and after (diamond data points) having been treated as described in Example 4;

FIG. 4 b is a pore size distribution plot obtained using non-linear density functional theory of the material produced in Example 4;

FIG. 5 a is a graph depicting argon physisorption isotherms of CBV 500 before (square data points) and after (diamond data points) having been treated as described in Example 5;

FIG. 5 b is a pore size distribution plot obtained using non-linear density functional theory of the material produced in Example 5;

FIG. 6 a is a graph depicting argon physisorption isotherms of CBV 500 before (square data points) and after (diamond data points) having been treated as described in Example 6;

FIG. 6 b is a pore size distribution plot obtained using non-linear density functional theory of the material produced in Example 6;

FIG. 7 a is a graph depicting argon physisorption isotherms at 87K of CBV 500 before (diamond data points) and after (square data points) having been treated as described in Example 7;

FIG. 7 b is a pore size distribution plot obtained using non-linear density functional theory of the material produced in Example 7;

FIG. 8 a is a graph depicting argon physisorption isotherms at 87K of CBV 500 before (diamond data points) and after (square data points) having been treated as described in Example 8;

FIG. 8 b is a pore size distribution plot obtained using non-linear density functional theory of the material produced in Example 8;

FIG. 9 a is a graph depicting argon physisorption isotherms at 87K of CBV 500 before (square data points) and after (diamond data points) having been treated as described in Example 9;

FIG. 9 b is a pore size distribution plot obtained using non-linear density functional theory of the material produced in Example 9;

FIG. 10 is a graph depicting an argon physisorption isotherm at 77K of CBV 300 having been treated as described in Example 10;

FIG. 11 a is a TEM micrograph of the material prepared in Example 10; and

FIG. 11 b is a TEM micrograph of the material prepared in Example 10.

DETAILED DESCRIPTION

Various embodiments of the present invention concern methods for preparing a material containing a mesostructured zeolite. In one or more embodiments, the mesostructured zeolite can be prepared by first subjecting an initial zeolite to an acid wash and thereafter forming at least one mesopore in the resulting acid-washed zeolite. In various other embodiments, the initial zeolite can be subjected to isomorphic substitution so as to replace at least a portion of the initial zeolite' s framework aluminum atoms with framework silicon atoms. Thereafter, the isomorphically-substituted zeolite can be subjected to one or more processes for forming at least one mesopore in the zeolite.

As just mentioned, an initial zeolite can be employed as a starting material in preparing a mesostructured zeolite. In one or more embodiments, the initial zeolite can be a non-mesostructured zeolite. In other various embodiments, the initial zeolite can be a non-mesoporous zeolite. As used herein, the term “non-mesoporous” shall denote a composition having a total volume of less than 0.05 cc/g of 20 to 80 Å diameter mesopores. In one or more embodiments, initial zeolite starting materials can have a total 20 to 80 Å diameter mesopore volume of less than 0.01 cc/g. Additionally, suitable initial zeolites can have a total 1 to 20 Å micropore volume of at least 0.3 cc/g. Furthermore, the initial zeolite can have an average unit cell size of at least 24.40, at least 24.45, or at least 24.50 Å.

In various embodiments, the initial zeolite can have a low silicon-to-aluminum ratio (“Si/Al”). For example, the initial zeolite can have an Si/Al ratio of less than 30, less than 25, less than 20, less than 15, or less than 10, taking into consideration the total amount of aluminum in the zeolite (i.e., both framework and extra-framework aluminum). Additionally, the initial zeolite can have an Si/Al ratio in the range of from about 1 to about 30, in the range of from about 2 to about 20, or in the range of from 3 to 10. Furthermore, in various embodiments, the initial zeolite can have a high EFAL content. In one or more embodiments, the initial zeolite can have an EFAL content of at least 25, at least 30, at least 35, or at least 40 percent.

The type of zeolite suitable for use as the initial zeolite is not particularly limited. However, in one or more embodiments, the initial zeolite can be a Y zeolite (a.k.a., faujasite). Additionally, the initial zeolite can be an ultra-stable Y zeolite (“USY”). Specific examples of commercially-available Y zeolites suitable for use include, but are not limited to, USY CBV 500 and USY CBV 300, both available from Zeolyst International. Furthermore, the initial zeolite can be fully crystalline and can have long-range crystallinity.

As noted above, the initial zeolite can be pretreated with an acid wash prior to being exposed to the method of mesoporosity incorporation. Without being restricted to any specific theory, it is hypothesized that the difficulty of mesoporosity introduction in low Si/Al zeolites can be caused by i) the presence of a relatively high EFAL content that partially blocks the incorporation of mesoporosity in the zeolite, and/or ii) the higher Al content in the zeolite framework makes the local rearrangement needed to accommodate the pore forming agent in the zeolite more difficult (Si-O-Al bonds are less labile in basic pH than Si—O—Si bonds). Both properties may contribute to the more difficult introduction of mesoporosity in low Si/Al zeolites.

In one or more embodiments, the initial zeolite can be acid washed by exposing the zeolite in a solution containing an acid for a certain amount of time and temperature. The acid employed during the acid wash can be any known or hereafter discovered mineral acid, organic acid, or mixtures or two or more thereof. Furthermore, in various embodiments, the acid employed can also be a chelating agent. Additionally, one or more complexing agents (such as fluoride) can be employed during the acid wash. Specific examples of acids suitable for use in the various embodiments described herein include, but are not limited to, hydrochloric acid, hydrofluoric acid, sulfuric acid, nitric acid, acetic acid, sulfonic acid, oxalic acid, citric acid, ethylenediaminetetraacetic acid (“EDTA”), and mixtures of two or more thereof. In one or more embodiments, the acid comprises citric acid. When a chelating agent is employed, such chelating agent can also be used to treat the initial zeolite simultaneously with the below-described procedures for mesopore incorporation (e.g., the chelating agent can be included in the same reaction medium as the pH controlling medium and pore forming agent).

In one or more embodiments, a buffer solution can be employed during the acid wash that uses a weak acid in combination with a weak acid salt to give a constant pH. For example, in one embodiment citric acid can be used with ammonium citrate to produce a constant pH, but other weak acids and weak acid salts can be used.

During the acid wash, the acid can be present in an amount in the range of from about 1 to about 10, or in the range of from 1.5 to 4 milliequivalents per gram of initial zeolite. Additionally, the acid-containing solution employed for the acid wash can have a pH in the range of from about 1 to about 6. Furthermore, the acid wash can be performed at a temperature in the range of from about 20 to about 100° C. Moreover, the acid wash can be performed over a time period ranging from about 5 minutes to about 12 hours, or in the range of from 30 minutes to 2 hours. In one or more embodiments, the initial zeolite is not steamed prior to acid washing.

In one or more embodiments, following the acid wash, the acid-washed zeolite can be vacuum filtered and washed with water. After the water wash, the acid-washed zeolite can be filtered again. Any filtering and washing techniques known or hereafter discovered in the art may be employed for these steps.

Without being restricted to any particular theory, it appears that acid washing the initial zeolite opens some Si—O—Al bonds in the zeolite framework, creating Si—OH and Al—OH terminal groups on the surface of the zeolite. This seems to make the acid-washed zeolite more reactive and therefore the incorporation of mesoporosity easier. Accordingly, in one or more embodiments, the acid-washed zeolite can have fewer Si—O—Al bonds in its zeolite framework than the above-described initial zeolite. In various embodiments, the acid-washed zeolite can have at least 0.1, at least 1, at least 5, or at least 10 percent fewer Si—O—Al bonds than the initial zeolite. Furthermore, the acid-washed zeolite can have a greater number of Si—OH and/or Al—OH terminal groups than the initial zeolite. In various embodiments, the acid-washed zeolite can have at least 0.1, at least 1, at least 5, or at least 10 percent more Si—OH and/or Al—OH terminal groups than the initial zeolite.

Furthermore, the resulting acid-washed zeolite can have a decreased aluminum content. However, in one or more embodiments, the aluminum content of the acid-washed zeolite can be maintained in an amount sufficient to preserve the unit cell size of the acid-washed zeolite at a minimum of at least 24.30, 24.35, or 24.40 Å.

In addition or in the alternative to the above-described acid wash procedure, the initial zeolite can subjected to a procedure for isomorphically substituting at least a portion of the initial zeolite' s framework aluminum with framework silicon. In one or more embodiments, such substitution can be accomplished by chemical treatment with an isomorphic substitution agent, such as, for example, ammonium hexafluorosilicate or silicon tetrachloride. In various embodiments, the isomorphic substitution agent can be in liquid form and/or vapor form during treatment. This treatment is effective to increase the Si/A1 ratio without causing significant EFAL, thus allowing greater mesopore formation in the resulting isomorphically-substituted zeolite. As evidence of this, FIG. 1 depicts nitrogen physisorption isotherms at 77K of zeolite before (square data points) and after (diamond data points) having been treated with ammonium hexafluorosilicate. FIG. 1 indicates an increase in mesopore volume of the isomorphically-substituted zeolite beginning at approximately 0.3 relative pressure. In one or more embodiments, the isomorphic substitution of the initial zeolite can cause an increase in the Si/Al ratio of at least 1, at least 5, at least 10, at least 20, at least 50, or at least 100 percent.

Various embodiments of the present technology can also include an additional step of controlled drying of the acid-washed zeolite prior to the below-described mesopore incorporation. Herein, it is shown that selective drying allows for further tuning the incorporation of controlled mesoporosity in zeolites while maintaining a desired amount of microporosity. In some embodiments, the amount of microporosity and mesoporosity in low Si/Al zeolites can be controlled during pretreatment by using different drying conditions following acid wash treatment.

As noted above, it appears that the previously-described acid washing opens some Si—O—Al bonds in the zeolite framework, creating Si—OH and Al—OH terminal groups on the surface of the zeolite. This seems to make the acid-washed zeolite more reactive and therefore the incorporation of mesoporosity easier. Though not wishing to be bound by theory, it appears that severe drying conditions (for example, 80° C. overnight, but other drying conditions can be used) manage to condense some of the hydroxyl terminal groups created during the acid treatment thereby eliminating at least some of the added reactivity of the zeolite. Increases in the severity of the drying conditions can allow for incorporating significant mesoporosity, while maintaining a high degree of microporosity in the zeolite. By increasing the severity of drying conditions, a higher amount of crystallinity and unit cell size (“UCS”) can be preserved.

In one or more embodiments, the optional drying step can include drying at a temperature of at least 20, at least 50, or at least 80° C. Additionally, the drying step can be performed at a temperature in the range of from about 20 to about 150° C., in the range of from about 50 to about 120° C., or in the range of from 70 to 90° C. Furthermore the drying step can be performed for a time period of at least 5 minutes, at least 30 minutes, or at least 1 hour. In other embodiments, the drying step can be performed for a time period in the range of from about 5 minutes to about 24 hours, in the range of from about 15 minutes to about 12 hours, or in the range of from 30 minutes to 2 hours.

In still other embodiments, the drying step can be omitted entirely. In other words, after filtering the acid-washed zeolite, the resulting wet cake can be directly subjected to the below-described mesopore formation process.

As mentioned above, the pretreated (e.g., acid-washed and/or isomorphically substituted) initial zeolite can be subjected to a mesopore formation process in order to form at least one mesopore in the pretreated initial zeolite. Methods for mesopore incorporation contemplated by various embodiments of the present technology (e.g., introduction of mesoporosity in zeolites) can generally include the following steps:

-   -   1. Contacting the pretreated zeolite with a pH controlling         medium in the presence of a pore forming agent under various         time and temperature conditions.     -   2. Filter, wash, and dry the zeolite.     -   3. Remove and/or recover the pore forming agent, for example by         calcination (removal) and/or chemical extraction (recovery).     -   4. The resulting material can also be chemically modified (for         example by ion exchange with rare earths), blended with binders,         matrix, and additives, and shaped (for example, in beads,         pellets, FCC catalysts).

In one or more embodiments, the mesopore formation process can be performed employing any reagents and under any conditions described in U.S. Published Patent Application No. 2007/0244347, the entire disclosure of which is incorporated herein by reference. For example, the temperature employed during mesopore formation can range from about room temperature to about 200° C. The time period employed can be in the range of from about 2 hours to about 2 weeks. Furthermore, the pH controlling medium can have a pH in the range of from about 9 to about 11. In one or more embodiments, the pH controlling medium can comprise a base, such as, for example, ammonium hydroxide. Additionally, the pore forming agent can include a surfactant. When basic conditions are employed, typically a cationic surfactant can be used, such as a cetyltrimethyl ammonium halide (e.g., cetyltrimethyl ammonium bromide (“CTAB”)).

Following the contacting step, the zeolite can be filtered, washed, and/or dried. In one or more embodiments, the zeolite can be filtered via vacuum filtration and washed with water. Thereafter, the recovered zeolite can optionally be filtered again and optionally dried.

Following the filter, wash, and drying steps, the zeolite can be subjected to heat treatment or chemical extraction in order to remove or recover at least a portion of the pore forming agent. In one or more embodiments, the zeolite can be calcined in nitrogen at a temperature in the range of from about 500 to about 600° C., and then in air for pore forming agent (e.g., surfactant) removal. The pore forming agent removal technique is selected based, for example, on the time needed to remove all of the pore forming agent from the zeolite. The total time period employed for heat treatment of the zeolite can be in the range of from about 30 minutes to about 24 hours, or in the range of from 1 to 12 hours.

The resulting mesostructured zeolite can be a one-phase hybrid single crystal having long range crystallinity. In one or more embodiments, the mesostructured zeolite can be fully crystalline, and can include mesopore surfaces defining a plurality of mesopores. A cross-sectional area of each of the plurality of mesopores can be substantially the same. In various embodiments, the mesostructured zeolite can have a total 20 to 80 Å diameter mesopore volume of at least 0.05, 0.1, 0.15, or 0.2 cc/g. Additionally, the mesostructured zeolite can have a total 20 to 80 Å diameter mesopore volume in the range of from about 0.05 to about 0.4, or in the range of from 0.1 to 0.3 cc/g.

As noted above, various techniques described herein can be employed to control or maintain the microporosity of the mesostructured zeolite. In one or more embodiments, the mesostructured zeolite can have a total 1 to 20 Å diameter micropore volume of less than 3.0, less than 2.5, less than 2.0, less than 1.5, or less than 1.0 cc/g. Additionally, the mesostructured zeolite can have a total 1 to 20 Å diameter micropore volume in the range of from about 0.001 to about 3.0, in the range of from about 0.01 to about 2.0, or in the range of from 0.05 to 1.0 cc/g.

In one or more embodiments, the mesostructured zeolite can have an average unit cell size of at least 24.30, 24.35, or 24.40 Å.

In the present technology, it is contemplated that low Si/Al USY mesostructured zeolites can also be prepared by realuminating high Si/Al mesostructured zeolites, such as those described in U.S. Patent Application Publication Number 2007/0244347 from CBV 720. Any methods known or hereafter discovered in the art for aluminating a zeolite can be employed in this embodiment.

The following examples are intended to be illustrative of the present invention in order to teach one of ordinary skill in the art to make and use the invention and are not intended to limit the scope of the invention in any way.

EXAMPLES Example 1 No Pretreatment of CBV 720

8 g of CBV 720 were added to a clear solution containing 50 mL of deionized water, 15 mL of an NH₄OH aqueous solution (30 wt %), and 4 g of cetyltrimethyl ammonium bromide (“CTAB”) to form a suspension. The suspension was treated in a sealed vessel at 80° C. for 24 hrs. After this time, the solid was filtered out, washed with deionized water, dried at room temperature overnight, and heat treated. During heat treatment, the sample was heated in a nitrogen atmosphere from room temperature to 550° C. in 4 hours, the sample was held at 550° C. for 2 hours, and then dried in air for 8 hours at 550° C.

This treatment produced the incorporation of a significant amount of mesoporosity (over 0.2 cc/g) with a controlled pore size (2-8 nm). The sample was tested by nitrogen physisorption at 77K (FIGS. 2 a and 2 b).

Example 2 No Pretreatment of CBV 500

8 g of CBV 500 were added to a clear solution containing 50 mL of deionized water, 15 mL of an NH₄OH aqueous solution (30 wt %), and 4 g of CTAB to form a suspension. The suspension was treated in a sealed vessel at 80° C. for 24 hrs. After this time, the solid was filtered out, washed with deionized water, dried at room temperature overnight, and heat treated. During heat treatment the sample was heated in a nitrogen atmosphere from room temperature to 550° C. in 4 hours, held at 550° C. for 2 hours, and then dried in air for 8 hours at 550° C.

This treatment did not produce any significant mesoporosity in the final material, as tested by argon physisorption at 87K (FIGS. 3 a and 3 b).

Example 3 No Pretreatment of CBV 300

8 g of CBV 300 were added to a clear solution containing 50 mL of deionized water, 15 mL of an NH₄OH aqueous solution (30 wt %), and 4 g of CTAB to form a suspension. The suspension was treated in a sealed vessel at 80° C. for 24 hrs. After this time, the solid was filtered out, washed with deionized water, dried at room temperature overnight, and heat treated. During heat treatment the sample was heated in a nitrogen atmosphere from room temperature to 550° C. in 4 hours, held at 550° C. for 2 hours, and then dried in air for 8 hours at 550° C.

This treatment did not produce any significant mesoporosity in the final material.

Example 4 Acid Wash Pretreatment of CBV 500

25 g of dried CBV 500 were added to a solution containing 750 mL deionized water containing 6.4 g of citric acid to form a suspension. The suspension was stirred for 30 min. at room temperature. The solid was vacuum filtered and washed using 750 mL H₂O and the solid was filtered again. The filter cake was recovered and dried at 80° C. overnight. Then the solid was sieved and 22.90 g of solid were recovered.

22.8 g of the recovered, pre-treated CBV 500 solid were added to a clear solution containing 152 mL deionized water, 46 mL NH₄OH, and 9.1 g of CTAB to form a suspension. The suspension was treated in a sealed vessel at 80° C. for 24 hrs. Then, the solid was filtered out and the cake was washed with deionized water (in situ washing 3×300 mL H₂O). The filtered cake was removed and dried in an oven overnight at 80° C. The sample was heated in nitrogen atmosphere at 550° C. for 2 hrs and then heated at 600° C. in air for 4 hrs.

This treatment produced a small amount of mesoporosity, while retaining a significant amount of microporosity as tested with argon adsorption (FIGS. 4 a and 4 b).

Example 5 Acid Wash Pretreatment of CBV 500

A solution of 25 g citric acid and 750 mL deionized water was prepared. The solution was stirred for 10 min. A first 8.33 g of CBV 500 were added to the solution and stirred for 10 min. A second 8.33 g of CBV 500 were added to the suspension and was then stirred for an additional 10 min. A third 8.33 g of CBV 500 were added to the suspension and was then stirred for an additional 10 min. Thus, a total of 25 g of CBV 500 were stirred into the citric acid/deionized water solution. Then the total suspension was stirred for 1 hr. The suspension was transferred to a vacuum filter unit, where it was filtered and washed in situ using 750 mL H₂O. The recovery was dried in an oven at 80° C. overnight.

19.88 g of the above solid were added to a clear solution containing 133 mL H₂O, 40 mL NH₄OH, and 7.95 g CTAB. The suspension was treated in a sealed vessel at 80° C. for 24 hrs. After this time, the solid was filtered out and washed with deionized water in situ. The filter cake was recovered and dried in an oven overnight at 80° C. The sample was heated in nitrogen atmosphere at 550° C. for 2 hrs and then heated at 600° C. in air for 4 hrs.

This treatment caused high reduction of zeolite microporosity, but did not introduce a significant amount of mesoporosity as tested by argon physisorption (FIGS. 5 a and 5 b).

Example 6 Acid Wash Pretreatment of CBV 500

25 g of CBV 500 zeolite were added in 375 mL H₂O containing 8 g citric acid to form a suspension. The suspension was stirred for 30 min. at room temperature. The solid was vacuum filtered and then washed using 375 mL H₂O and then filtered. The filter cake was recovered and dried in an oven at 80° C. for 24 hrs. Then the recovered pre-treated CBV 500 solid that was recovered from the filter cake was sieved.

21.86 g of the above solid were added to a clear solution containing 146 mL H₂O, 44 mL NH₄OH, and 8.74 g CTAB to form a suspension. The suspension was treated in a sealed vessel at 80° C. for 24 hrs. After this time the solid was filtered out and washed with deionized water. The filter cake was recovered and dried in an oven overnight at 80° C. The sample was heated in nitrogen atmosphere at 550° C. for 2hrs and then heated at 600° C. under air for 4 hrs.

This treatment caused a small reduction of zeolite microporosity, while introducing a reasonable amount of mesoporosity (FIGS. 6 a and 6 b).

Example 7 Acid Wash Pretreatment of CBV 500 with 1 Hour Drying at 20° C.

25 g of CBV 500 zeolite were added in 375 mL H₂O containing 9.5 g citric acid to form a suspension. The suspension was stirred for 30 min. at room temperature. The solid was vacuum filtered and washed using 375 mL H₂O. The filter cake was recovered and dried under air for 1 hr. Then the recovered pre-treated CBV 500 solid recovered from the filter cake was sieved.

25 g of the wet cake were added to a clear solution containing 167 mL H₂O, 50 mL NH₄OH, and 10 g CTAB. The suspension was treated in a sealed vessel at 80° C. for 24 hrs. After this time the solid was filtered out and washed with deionized water. The filter cake was recovered and air dried overnight. The sample was heated in nitrogen atmosphere at 550° C. for 2 hrs and then heated at 600° C. under air for 4 hrs.

This treatment caused high reduction of zeolite microporosity, while introducing a significant amount of mesoporosity (FIGS. 7 a and 7 b).

Example 8 Acid Wash Pretreatment of CBV 500 with 1 Hour Drying at 80° C.

25 g of CBV 500 zeolite were added in 375 mL H₂O containing 9.5 g citric acid to form a suspension. The suspension was stirred for 30 min. at room temperature. The solid was vacuum filtered and washed using 375 mL H₂O. The filter cake was recovered and dried at 80° C. for 1 hr. Then the recovered pre-treated CBV 500 solid recovered from the filter cake was sieved.

15.38 g of the wet cake were added to a clear solution containing 102 mL H₂O, 31 mL NH₄OH, and 6.15 g CTAB to form a suspension. The suspension was treated in a sealed vessel at 80° C. for 24 hrs. After this time the solid was filtered out and washed with deionized water. The filter cake was recovered and dried in an oven overnight at 80° C. The sample was heated in nitrogen atmosphere at 550° C. for 2 hrs and then heated at 600° C. under air for 4 hrs.

This treatment caused high retention of zeolite microporosity, while introducing a smaller amount of mesoporosity than in the case of Example 7 (FIGS. 8 a and 8 b).

Example 9 Acid Wash Pretreatment of CBV 500 with 24 Hour Drying at 80° C.

25 g of CBV 500 zeolite were added in 375 mL H₂O containing 8 g citric acid to form a suspension. The suspension was stirred for 30 min. at room temperature. The solid was vacuum filtered and washed using 375 mL H₂O. The filter cake was recovered and dried in an oven at 80° C. for 24 hrs. Then the recovered pre-treated CBV 500 solid recovered from the filter cake was sieved.

21.86 g of the above solid were added to a clear solution containing 146 mL H₂O, 44 mL NH₄OH, and 8.74 g CTAB to form a suspension. The suspension was treated in a sealed vessel at 80° C. for 24 hrs. After this time the solid was filtered out and washed with deionized water. The filter cake was recovered and dried in an oven overnight at 80° C. The sample was heated in nitrogen atmosphere at 550° C. for 2 hrs and then heated at 600° C. under air for 4 hrs.

This treatment caused higher retention of zeolite microporosity, while introducing an even smaller amount of mesoporosity than it the case of Example 8 (FIGS. 9 a and 9 b).

Characterization Results for Examples 7-9

Argon adsorption was used in order to characterize the samples of Examples 7-9 in terms of their pore size distribution. Pore widths lower than 20 Å are considered to be microporosity, while pore widths from 20 to 80 Å are considered to be mesoporosity introduced by the technique herein described. In Table 2, the micro- and mesoporosity as well as the total pore volume of the three materials described in Examples 7-9 are given. For comparison, the micro- and mesoporosity of the original CBV 500 sample are shown. In Table 3, the crystallinity and the UCS of the materials described in Examples 7-9 are presented.

As shown in Table 2, as the severity of the drying conditions increases the amount of microporosity preserved. This is consistent with the theory of reduction in reactivity of the samples dried at higher temperatures. These conditions can be optimized. Very mild conditions (20° C., 1 h) causes the loss of most of the microporosity (from 0.32 to 0.072 cc/g), whereas more severe drying conditions (80° C., 24 h) causes a significant reduction in the mesoporosity introduced (0.222 to 0.110 cc/g), with improvement in the microporosity (0.224 compared to 0.072 cc/g).

TABLE 2 Micro-, Meso-, and Total Pore Volume for CBV 500 and Examples 7-9 Micropore Mesopore Drying Volume (cc/g) Volume (cc/g) Total Pore Sample conditions <20 Å 20-80 Å Volume (cc/g) CBV 500 — 0.320 negligible 0.320 Example 20° C., 0.072 0.222 0.301 #7 1 h Example 80° C., 0.202 0.209 0.428 #8 1 h Example 80° C., 0.224 0.110 0.351 #9 24 h

TABLE 3 Crystallinity and Unit Cell Size for CBV 500 and Examples 7-9 Sample Drying conditions UCS (Å) Crystallinity, % CBV 500 — 24.552 92.6 Example #7 20° C., 1 h — — Example #8 80° C., 1 h 24.423 56.7 Example #9 80° C., 24 h 24.446 71.7

Example 10 Isomorphic Substitution Pretreatment of CBV 300

5 g of NH₄Y zeolite (CBV 300 from Zeolyst International) were added to 250 mL of 3M ammonium acetate. To this mixture was added 24.5 mL of 0.4M ammonium hexafluorosilicate solution dropwise for 1 hour while stirring. The resulting solid was vacuum filtered and washed with H₂O.

21.86 g of the wet cake were added to a clear solution containing 146 mL H₂O, 44 mL NH₄OH, and 87.4 g CTAB to form a suspension. The suspension was treated in a sealed vessel at 80° C. for 24 hrs. After this time the solid was filtered out and washed with deionized water. The filter cake was recovered and dried in an oven overnight at 80° C. The sample was heated in nitrogen atmosphere at 550° C. for 2 hrs and then heated at 600° C. under air for 4 hrs.

FIG. 10 is a graph depicting an argon physisorption isotherm at 77K of the resulting mesostructured zeolite. As can be seen in FIG. 10, the mesostructured zeolite displays an increased mesopore volume beginning at approximately 0.3 relative pressure.

FIGS. 11 a and 11 b are TEM micrographs of the material prepared in this Example.

Selected Definitions

It should be understood that the following is not intended to be an exclusive list of defined terms. Other definitions may be provided in the foregoing description accompanying the use of a defined term in context.

As used herein, the terms “a,” “an,” and “the” mean one or more.

As used herein, the term “and/or,” when used in a list of two or more items, means that any one of the listed items can be employed by itself or any combination of two or more of the listed items can be employed. For example, if a composition is described as containing components A, B, and/or C, the composition can contain A alone; B alone; C alone; A and B in combination; A and C in combination; B and C in combination; or A, B, and C in combination.

As used herein, the terms “comprising,” “comprises,” and “comprise” are open-ended transition terms used to transition from a subject recited before the term to one or more elements recited after the term, where the element or elements listed after the transition term are not necessarily the only elements that make up the subject.

As used herein, the terms “containing,” “contains,” and “contain” have the same open-ended meaning as “comprising,” “comprises,” and “comprise” provided above.

As used herein, the terms “having,” “has,” and “have” have the same open-ended meaning as “comprising,” “comprises,” and “comprise” provided above.

As used herein, the terms, “including,” “include,” and “included” have the same open-ended meaning as “comprising,” “comprises,” and “comprise” provided above.

Unless otherwise indicated, the term “mesoporous” is art-recognized and refers to a porous material comprising pores with an intermediate size, ranging anywhere from about 2 to about 50 nanometers.

The term “mesostructure” is art-recognized and refers to a structure comprising mesopores which control the architecture of the material at the mesoscopic or nanometer scale, including ordered and non-ordered mesostructured materials, as well as nanostructured materials, i.e., materials in which at least one of their dimensions is in the nanometer size range, such as nanotubes, nanorings, nanorods, nanowires, nanoslabs, and the like.

The term “mesostructured zeolites” as used herein includes all crystalline mesoporous materials, such as zeolites, aluminophosphates, gallophosphates, zincophosphates, titanophosphates, etc. Its mesostructure maybe in the form of ordered mesporosity (as in, for example MCM-41, MCM-48 or SBA-15), non-ordered mesoporosity (as in mesocellular foams (MCF)), or mesoscale morphology (as in nanorods and nanotubes). The notation zeolite[mesostructure] is used to designate the different types of mesostructured zeolites.

“Y” represents a faujasite which is a zeolite comprising 2 moles of sodium and 1 mole of calcium in its octahedral crystal structure. This term also includes the acidic form of Y which may also be represented as “H—Y.”

The term “zeolite” is defined as in the International Zeolite Association Constitution (Section 1.3) to include both natural and synthetic zeolites as well as molecular sieves and other microporous and mesoporous materials having related properties and/or structures. The term “zeolite” also refers to a group, or any member of a group, of structured aluminosilicate minerals comprising cations such as sodium and calcium or, less commonly, barium, beryllium, lithium, potassium, magnesium and strontium; characterized by the ratio (Al+Si):O=approximately 1:2, an open tetrahedral framework structure capable of ion exchange, and loosely held water molecules that allow reversible dehydration. The term “zeolite” also includes “zeolite-related materials” or “zeotypes” which are prepared by replacing Si.sup.4+ or Al.sup.3+ with other elements as in the case of aluminophosphates (e.g., MeAPO, SAPO, ElAPO, MeAPSO, and ElAPSO), gallophosphates, zincophophates, titanosilicates, etc. 

What is claimed is:
 1. A method of forming a material comprising at least one mesoporous zeolite, said method comprising the steps of: (a) acid washing a non-mesoporous initial zeolite with an acidic medium thereby forming an acid-washed zeolite, wherein said initial zeolite has a total silicon-to-aluminum (Si/Al) ratio of less than 30, wherein said acid washing of step (a) removes aluminum atoms from said initial zeolite such that said acid-washed zeolite has a higher Si/Al ratio than said initial zeolite; and (b) subsequent to step (a), contacting said acid-washed zeolite with a mesopore-forming medium different than said acidic medium thereby forming at least one mesopore within said acid-washed zeolite and providing said mesoporous zeolite.
 2. The method of claim 1, wherein said initial zeolite has a Si/Al of less than
 10. 3. The method of claim 1, wherein said acidic medium does not comprise hydrofluoric acid.
 4. The method of claim 1, wherein said acidic medium comprises at least one acid selected from the group consisting of chlorhidric acid, sulphuric acid, nitric acid, acetic acid, sulfonic acid, oxalic acid, ethylenediaminetetraacetic acid (EDTA), citric acid, and combinations thereof
 5. The method of claim 1, wherein said acid-washed zeolite has at least 1 percent fewer Si—O—Al bonds than said initial zeolite.
 6. The method of claim 1, wherein said acid-washed zeolite has a greater number of Si—OH and/or Al—OH terminal groups than said initial zeolite.
 7. The method of claim 1, wherein the total pore volume of said mesoporous zeolite is greater that the total pore volume of said acid-washed zeolite.
 8. The method of claim 1, wherein said mesoporous zeolite has an increased mesoporosity and a decreased microporosity relative to said acid-washed zeolite.
 9. The method of claim 1, wherein said initial zeolite has a total 20 to 80 Å diameter mesopore volume of less than 0.05 cc/g, wherein said mesoporous zeolite has a total 20 to 80 Å diameter mesopore volume of at least 0.1 cc/g.
 10. The method of claim 9, wherein the total 1 to 20 Å diameter micropore volume of said mesoporous zeolite is less than the total 1 to 20 Å diameter micropore volume of said acid-washed zeolite.
 11. The method of claim 10, wherein said initial zeolite has a total 1 to 20 Å diameter micropore volume of at least 0.3 cc/g.
 12. The method of claim 1, wherein said initial zeolite has an average unit cell size of at least 24.40 Å and said acid-washed zeolite has an average unit cell size of at least 24.35 Å.
 13. The method of claim 1, wherein said mesoporous zeolite is a mesostructured zeolite, a one-phase hybrid single crystal having long-range crystallinity.
 14. The method of claim 1, wherein said acid washing is performed at a temperature of not more than 100° C., wherein said acid washing is performed for a time period of not more than 12 hours.
 15. The method of claim 1, wherein said acidic medium comprises an acid that is present in an amount in the range of from about 1 to about 10 milliequivalents per gram of initial zeolite.
 16. The method of claim 1, wherein said acidic medium comprises a chelating agent.
 17. The method of claim 16, wherein said chelating agent is selected from the group consisting of oxalic acid, citric acid, and ethylenediaminetetraacetic acid (EDTA).
 18. The method of claim 1, wherein said acidic medium is in liquid form during said acid-washing.
 19. The method of claim 1, wherein said mesopore-forming medium is basic.
 20. The method of claim 19, wherein said mesopore-forming medium comprises at least one surfactant.
 21. The method of claim 1, further comprising, prior to said contacting of step (b), drying said acid-washed zeolite at a drying temperature greater than 20° C. for a drying time greater than 1 hour.
 22. The method of claim 1, further comprising realuminating said mesoporous zeolite to thereby lower the Si/Al ratio of said mesoporous zeolite.
 23. The method of claim 1, further comprising blending said mesoporous zeolite with a binder, a matrix, and/or an additive to thereby form a blended material, further comprising shaping said blended material into a catalyst composition.
 24. The method of claim 1, wherein said material is a catalyst composition.
 25. The method of claim 24, wherein said catalyst composition is a cracking catalyst.
 26. The method of claim 25, wherein said cracking catalyst is a fluid catalytic cracking (FCC) catalyst.
 27. A method of forming a material comprising at least one mesoporous zeolite, said method comprising the steps of: (a) contacting an initial zeolite with an acidic medium to thereby form an acid-treated zeolite, wherein said initial zeolite has a total silicon-to-aluminum (Si/Al) ratio of less than 15, wherein said acidic medium does not comprise hydroflouric acid; and (b) subsequent to step (a), forming at least one mesopore within said non-mesoporous acid-treated zeolite thereby forming a mesoporous zeolite.
 28. The method of claim 27, wherein said acidic medium comprises at least one acid selected from the group consisting of chlorhidric acid, sulphuric acid, nitric acid, acetic acid, sulfonic acid, oxalic acid, ethylenediaminetetraacetic acid (EDTA), citric acid, and combinations thereof
 29. The method of claim 27, wherein said acidic medium comprises an acid that is present in an amount in the range of from about 1 to about 10 milliequivalents per gram of initial zeolite.
 30. The method of claim 27, wherein said acidic medium comprises a chelating agent.
 31. The method of claim 27, wherein said contacting of step (a) is carried out at a temperature of not more than 100° C. and for a time period of not more than 12 hours.
 32. The method of claim 27, wherein said contacting of step (a) removes aluminum atoms from said initial zeolite.
 33. The method of claim 32, wherein said acid-treated zeolite has a higher Si/Al ratio than said initial zeolite
 34. The method of claim 27, wherein said initial zeolite has a total silicon-to-aluminum ratio (Si/Al) of less than
 10. 35. The method of claim 27, wherein said mesoporous zeolite has an increased mesoporosity and a decreased microporosity relative to said acid-treated zeolite.
 36. The method of claim 27, wherein said initial zeolite has a total 20 to 80 Å diameter mesopore volume of less than 0.05 cc/g, wherein said mesoporous zeolite has a total 20 to 80 Å diameter mesopore volume of at least 0.1 cc/g.
 37. The method of claim 27, wherein said initial zeolite has an average unit cell size of at least 24.40 A and said acid-treated zeolite has an average unit cell size of at least 24.35 Å.
 38. The method of claim 27, wherein said acid-treated zeolite has at least 1 percent fewer Si—O—Al bonds than said initial zeolite.
 39. The method of claim 27, wherein said acid-treated zeolite has a greater number of Si—OH and/or Al—OH terminal groups than said initial zeolite.
 40. The method of claim 27, wherein said forming of step (b) comprises contacting said acid-treated zeolite with a medium comprising at least one base.
 41. The method of claim 40, wherein said medium further comprises at least one surfactant.
 42. The method of claim 27, wherein said acidic medium is in liquid form during said contacting.
 43. A method of forming a mesoporous zeolite, said method comprising: (a) contacting an initial zeolite an with an acidic medium to thereby form an acid-treated zeolite, wherein said initial zeolite has a total silicon-to-aluminum (Si/Al) ratio of less than 10, wherein said contacting of step (a) removes aluminum atoms from said initial zeolite such that said acid-treated zeolite has a higher Si/Al ratio than said initial zeolite and (b) subsequent to step (a), contacting said acid-treated zeolite with a basic medium to thereby provide a base-treated zeolite having have an increased volume of 20 to 80 Å diameter mesopores relative to said acid-treated zeolite, wherein said base-treated zeolite has a total 20 to 80 Å diameter mesopore volume of at least 0.1 cc/g.
 44. The method of claim 43, wherein said initial zeolite has a total 20 to 80 Å diameter mesopore volume of less than 0.05 cc/g.
 45. The method of claim 43, wherein the total 1 to 20 Å diameter micropore volume of said base-treated is less than the total 1 to 20 Å diameter micropore volume of said acid-treated zeolite.
 46. The method of claim 45, wherein said initial zeolite has a total 1 to 20 Å diameter micropore volume of at least 0.3 cc/g.
 47. The method of claim 43, wherein said initial zeolite has an average unit cell size of at least 24.40 Å and said acid-treated zeolite has an average unit cell size of at least 24.35 Å.
 48. The method of claim 43, wherein said acidic medium comprises an acid that is present in an amount in the range of from about 1 to about 10 milliequivalents per gram of initial zeolite.
 49. The method of claim 43, wherein said acidic medium does not comprise hydrofluoric acid.
 50. The method of claim 43, wherein said acidic medium comprises at least one acid selected from the group consisting of chlorhidric acid, sulphuric acid, nitric acid, acetic acid, sulfonic acid, oxalic acid, ethylenediaminetetraacetic acid (EDTA), citric acid, and combinations thereof
 51. The method of claim 43, wherein said acidic medium comprises a chelating agent.
 52. The method of claim 43, wherein said initial zeolite has an extra-framework aluminum content of 25% to 100%.
 53. The method of claim 43, wherein said acid-treated zeolite has at least 1 percent fewer Si—O—Al bonds than said initial zeolite.
 54. The method of claim 43, wherein said acid-treated zeolite has a greater number of Si—OH and/or Al—OH terminal groups than said initial zeolite.
 55. The method of claim 43, wherein said basic medium comprises a pore forming agent.
 56. The method of claim 55, wherein said pore forming agent comprises a surfactant.
 57. The method of claim 43, wherein said acidic medium is in liquid form during said contacting of step (a). 